Pengaruh Sudut Anyam Komposit Berpenguat Serat Pelepah Pisang dengan Matriks Unsaturated Polyester

Ardhi Harist Hirosana; Sri Hastuti; R. Faiz Listyanda

doi:10.61132/mars.v3i2.761

Authors

Ardhi Harist Hirosana Universitas Tidar
Sri Hastuti Universitas Tidar
R. Faiz Listyanda Universitas Tidar

DOI:

https://doi.org/10.61132/mars.v3i2.761

Keywords:

ASTM D638, banana ‘kepok’ stalk fibers, tensile testing

Abstract

The use of lightweight plastic materials is widely applied in the manufacturing of car dashboards. Lightweight plastics or polymers, such as ABS plastic, are not strong enough or can easily crack when impacted. Banana pseudostem fibers have good mechanical properties and are a potential reinforcement for composites. This study aims to analyze the tensile strength of unsaturated polyester-banana pseudostem fiber composites produced through the hand lay-up method at three different angles: 0°/90°, 15°/105°, and 30°/120°. The tensile testing refers to ASTM D638 standards. The results of the tensile tests show that the 0°/90° weaving angle variation had the highest tensile strength value, which was 372.07 MPa. The 30°/120° fiber orientation variation had the lowest tensile strength value at 198.12 MPa. The fractures from the tensile tests were observed through macro photos to understand the failure mode. The macro photo observations showed that all specimens experienced fiber pull-out.

References

Aldrino (2018). Studi Eksperimental Efek Plastik Limbah Tipe ABS Sebagai Agregat Pada Kuat Tekan Beton Dengan Semen PCC. Universitas Katolik Parahyangan, Bandung

Hastuti, S., Budiono, H. S., Ivadiyanto, D. I., & Nahar, M. N. (2021). Peningkatan Sifat Mekanik Komposit Serat Alam Limbah Sabut Kelapa (Cocofiber) yang Biodegradable. Reka Buana: Jurnal Ilmiah Teknik Sipil dan Teknik Kimia, 6(1), 30-37.

Herwandi, H., Sugianto, S., Somawardi, S., & Subhan, M. (2014). Pengaruh volume serat rekel terhadap kekuatan tarik dan impact komposit sebagai bahan pembuatan dashboard mobil. Prosiding Semnastek, 1(1).

Lelewati, Een Tonadi, Aan Sefentry (2023). Analisis Kekerasan Papan Komposit dari Serat Pelepah Pisang Dengan Resin Polyester. Jurnal online universitas PGRI Palembang,vol. 8.

Nurhidayat, A., & Wijoyo, W. (2014, September). Pengaruh Fraksi Volume Serat Cantula Terhadap Ketangguhan Impak Komposit Cantula-HDPE Daur Ulang Sebagai Bahan Core Lantai Ramah Lingkungan. In Seminar Nasional Teknologi dan Informatika 2014. Muria Kudus University.

Paundra, F. (2022). Analisis Kekuatan Tarik Komposit Hybrid Berpenguat Serat Batang Pisang Kepok dan Serat Pinang. Nozzle: Journal Mechanical Engineering, 11(1), 9-13.

Paundra, F., Chaniago, A. W., & Muhyi, A. (2022). Karakterisasi Pengaruh Sudut Anyaman Komposit Terhadap Kekuatan Tarik Serat Tandan Kosong Kelapa Sawit. Jurnal Crankshaft, 5(2).

Pramono, C. (2012). Pengaruh Perlakuan Alkali Kadar 5% dengan Lama Perendaman 0 Jam, 2jam, 4 Jam, 6 Jam terhadap Sifat Tarik Serat Pelepah Pisang Kepok. Jurnal Penelitian Inovasi, 37(1), 17777.

Rochardjo. (2023). Perkembangan Mutakhir Material Komposit, Peluang, Dan Tantangannya Dalam Aplikasi Di Bidang Otomotif. Pidato Pengukuhan Jabatan Guru Besar Fakultas Teknik Universitas Gadjah Mada.

Suharto, R. D., Darmo, A. N. S. H., & Listyanda, R. F. (2024). Pengaruh Orientasi Sudut Anyam Serat Bambu Petung Terhadap Kekuatan Mekanik dan Sifat fisik. Majamecha, 6(2), 197-202.